热塑性聚氨酯TPU

热塑性弹性体Thermoplastic Elastomer
产品说明Product description |
||||||||
TU55ST7是一款聚氨酯改性材料,具有特殊的止滑性。 TU55ST7is a polyurethane modified material with a special skid resistance. |
||||||||
关键特性Key characteristic |
||||||||
1.表面哑,手感柔软. The surface is mute and soft. 2..成型快、不粘模具 .Rapid molding,non-stick mold. 3.阻尼效果优异. Damping effect is good. 4可粘接材质ABS .PC .TPU Adhesive material:ABS, PC,TPU. |
||||||||
功能Function |
||||||||
产品应用 Main application |
手机保护套Phone protective cover |
|||||||
仪器外壳Instrument shell |
电子器件粘胶配件Electronic plastic accessories |
|||||||
加工方法Processing method |
注塑、挤出成型Injection and extrusion molding |
|||||||
环保认证 Environmental certification |
ROHS |
REACH |
EN71-3 |
|||||
PAHS |
ASTM-F963 |
Phthalate |
||||||
颜色Color |
本色Natural |
|||||||
气味Smell |
少许树脂味A little resin smell |
|||||||
外型Appearance |
圆球形小颗粒Cylindrical particle,about 3mm×1.5mm |
|||||||
储藏期Storage period |
常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months |
|||||||
包装方式Packaging method |
25公斤/袋 25kg/bag |
|||||||
物理性能Physical properties |
结果Result |
单位Unit |
方法Method |
成型条件Molding condition |
||||
比重Specific gravity |
1.2±0.02 |
g/cm3 |
ASTM D792 |
干燥温度Drying temp 80 ℃ |
||||
硬度Hardness |
56±3 |
shoreA |
ASTM D2240 |
干燥时间Drying time 2h |
||||
拉伸强度Tensile strength |
>5 |
Mpa |
ASTM D412 |
射嘴温度Nozzle temp 170℃ |
||||
断裂延伸Elongation at break |
>550 |
% |
ASTM D412 |
螺筒一段温度Screw 1 temp 160℃ |
||||
撕裂强度Tearing strength |
>20 |
Kn/m |
ASTM D624 |
螺筒二段温度Screw 2 temp 150℃ |
||||
熔融指数Melt index |
>40 |
g/10min |
ASTM D1238 |
螺筒三段温度Screw 3 temp 150℃ |
||||
注意事项Matters need attention |
||||||||
清洗料管 Purge compound |
需使用PP或 PE清洗干净机台螺杆,且把机台射嘴彻底清除干净please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean |
|||||||
着色 Coloring
|
请选择以PE或EVA为基材之色母,切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压,才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion |
|||||||
回收 Recycling |
二次料(水口料)回收比率建议最多10%。 Consistent regrind usage of up to 10% is permissible |